汽车挡风玻璃修补剂(渗透型)
Automotive windshield repair agent(penetration type)
汽车挡风玻璃修补剂(填补型)
Automotive windshield repair agent(filling type)
I. Brief introduction of the product:
Nanotechnology is adopted for the resin contained in this product, which is able to exhaust air in the hole and penetrate powerfully. Repair (star-type) damages and there shall be only a little circular mark or spider web crack (it can be observed from a special angle) left after repair completion. The strip (crack) will become an indistinct line, and the repair traces are not easy to be reserved.
II. Product function:
This product is dedicated to repairing broken holes, cracks, start-type and buphthalmus-type surface bruises on the windshield and front and rear headlamp glass of the vehicle.
Advantages:The repair is simple, convenient, rapid, and time and trouble saving, which can also be conducted at the site. After repair, the part is sturdy and durable with up to 98% definition. In order to prevent the broken hole or the crack from expanding, there is no need to assemble to avoid poor sealing and damages to the vehicle appearance due to glass replacement.
III. Instructions:(it is just for reference, because the repair tools of all brands have minor difference)
1. Confirm bruises and cracks before repair to check if they can be repaired.
2. This product is just used for the vehicle windshield, not used for glass that has been used for more than 10 years or glass of the manufacturer’s genuine product.
3. Because this product will harden under the effects of the ultraviolet light (sunlight), the operation must be conducted in sunny days. Prevent ultraviolet irradiation before injecting it into the glass.
4. Before construction, all parts to be repaired shall be cleaned and suffer from drying process under 10-20℃.
5. Insert the needle into the fracture to pick out fragments and then gradually expand the fracture little by little (to become convenient for injecting the repair agent).
6. Fix the transparent panel on the glass, and insert the nozzle to make it align with the fracture.
7. After injecting this product, insert the piston, repeatedly rotate it up and down until the fracture becomes indistinct and the paste the transparent film.
8. After it hardens after exposure to sunshine, use the blade to softly remove the excess repair agent.