MOF-FSA全合成切削液
MOF-FSA Total Synthesis Cutting Liquid
I. Product benefits
1. Lubrication: Good cleaning performance, which improves the surface quality of the workpiece, and excellent penetrating performance which can ensure the effective lubrication of the processed part.
2. Rust protection: With good rust protection for steel and nonferrous metals, it can fully satisfy high standards and requirements of rust protection.
3. Strong extreme pressure and anti-wear performance, which can prolong the service life of tools.
4. It adopts a fully synthesized formula without any toxin, odor, and irritant and in conformity with the requirements of environmental protection, and causes no environmental pollution.
II. Product usage
It is mainly applicable to the grilling, cutting, drilling, boring and other machining techniques of various steel and iron metals, and copper, aluminum, and magnesium.
III. MOF-FSA total synthesis cutting liquid (concentrated liquid) test report
Concentrated liquid | Name | Total synthesis cutting liquid for carbon steel, stainless steel, cast iron, copper and aluminum. | |||
Model | Total synthesis cutting liquid additive MOF--FSA | ||||
Appearance | Yellowish-brown transparent solution | ||||
Physical and chemical indicators | PH value | 9.9 | |||
Specific gravity | 1.26 | ||||
Pour point | Freeze at -22℃ | ||||
Flash point | Without flash points | ||||
Viscosity | 70.6883 mm2/s(40℃) | ||||
Test of storage stability | Test condition | Test results | |||
At constant 70℃ for 5 h. | No delamination and precipitation. | ||||
At constant -15℃ for 24 h. | No delamination and precipitation. | ||||
4000 rpm for 30 mins | No delamination and precipitation. | ||||
Dilution solution (5% concentrated liquid add water) | Appearance | Colorless clear liquid | |||
PH value | 9.2 | ||||
Anti-wear performance | Stuck in 14 blocks | ||||
Test of defoaming performance | Test condition | Test results | |||
Place 70 ml of diluent fluids in a 100 ml measuring cylinder, shake the cylinder f=up and down at a frequency of 100-120 times/min, and let it stand at room temperature for 10 minss (defoaming, when completed within 10 min, is deemed as qualified).. | Time of defoaming <1 min Qualified | ||||
Test of causticity | Test condition | Test results | |||
Copper | At constant 55℃ for 8 h. | Grade A is deemed as qualified | |||
Aluminum | At constant 55℃ for 8 hours. | Grade A is deemed as qualified | |||
Cast iron | At constant 55℃ for 24 h. | Grade A is deemed as qualified | |||
Test of rust protection | Test condition | Test results | |||
Monolithic | At constant 35℃ for 48 h. | No rust caused after five drops of fluid is deemed as qualified. | |||
Lamination | At constant 35℃ for 8 h. | No rust and overprint, up to standard | |||
Test of bacterial colonies | Dilute the diluent fluid with 0.5% saline solution by 10 times, place 1 ml of the fluid in the sterile petri dish, add in 20 ml of prepared medium, let it culture within the incubation at constant 30 ℃ for 24-48 h, and visually observe if the colony number qualifies. | ||||